Sikaflex® 554 300ml - black
Chemical base : Silane-terminated polymer (STP)
Cure Mechanism: Moisture curing A
Colour (CQP001-1): White, black
Density before curing: depending on colour; 1,44 kg/l
Working temperature: 5 °C to 40 °C
Skin forming time (CQP019-1): 25 minutes A
Volume change (CQP014-1): -2 %
Hardness Shore A (CQP023-1 / ISO 48-4): 55
Tensile strength (CQP036-1 / ISO 527): 3.5 MPa
Elongation at break (CQP036-1 / ISO 527): 500 %
Tear resistance (CQP045-1 / ISO 34): 20 N/mm
Tensile shear strength (CQP046-1 / ISO 4587): 2.5 MPa
Service temperature (CQP509-1 / CQP513-1): -50 to 90 °C
Storage: below 25 °C